Aim Ciprofloxacin polylactic acid microspheres (CFX-PLA-MS) were preparedusing solvent evaporation method from a solid-in-oil-in-water emulsion system. Methods Orthogonalexperiment was used to optimize the method of CFX-PLA-MS preparation. Microspheres werecharacterized in terms of morphology, size, encapsulation efficiency, drug loading and in vitro drugrelease. Results The physical state of CFX-PLA-MS was determined by scanning electron microscopy(SEM) and differential scanning calorimetry (DSC) . Microspheres formed were spherical with smoothsurfaces. Drug was enveloped in microspheres without mixing physically with PLA. The averageparticle size was 280.80 ± 0.15 μm, with over 90% of microspheres falling in the range of 250 -390 μm. The encapsulation efficiency was 65.8% ± 0.58% and the drug loading was 34.1% ± 0.51% .In vitro release study revealed a profile of sustained release of Ciprofloxacin from CFX-PLA-MS. Theaccumulated release percentage and half-life (T_(1/2) of Ciprofloxacin microspheres were 84.0% in53.2 h, and 31.9 h, respectively. Higuchi equation was Q= -0.0043 + 0.003 9 t^(1/2), r = 0.9941.Conclusion Ciprofloxacin microspheres have been successfully prepared and sustained release of CFXfrom microspheres is achieved.