A novel visible-light-responding InVO4-Cu2O-TiO2 ternary nanoheterostructure was designed on the basis of the strategy of energy gap engineering and prepared through ordinary wet chemistry methods. The as-prepared nanoheterostructure was characterized by X-ray powder diffraction（XRD）, transmission electron microscopy（TEM）, high-resolution transmission electron microscopy（HRTEM） and diffuse reflectance ultraviolet-visible spectroscopy（UV-vis/DRS）. The TEM and HRTEM images of 10%InVO4-40%Cu2O-50%TiO2 confirm the formation of nanoheterostructures resulting from contact of the nanosized TiO2, Cu2O and InVO4 in the size of 5–20 nm in diameter. The InVO4-Cu2O-TiO2 nanoheterostructure, when compared with TiO2, Cu2O, InVO4, InVO4-TiO2 and Cu2O-TiO2, shows significant enhancement in the photocatalytic performance for the degradation of methyl orange（MO） under visible-light irradiation. With a 9 W energy-saving fluorescent lamp as the visible-light source, the MO degradation rate of 10%InVO4-40%Cu2O-50%TiO2 reaches close to 90% during 5 h, and the photocatalytic efficiency is maintained at over 90% after six cycles. This may be mainly ascribed to the matched bandgap configurations of TiO2, Cu2O and InVO4, and the formations of two p-n junctions by the p-type semiconductor Cu2O with the n-type semiconductors TiO2 and InVO4, all of which favor spatial photogenerated charge carrier separation. The X-ray photoelectron spectroscopy（XPS） characterization for the used 10%InVO4-40%Cu2O-50%TiO2 reveals that only a small shakeup satellite peak appears for Cu（II） species, implying bearable photocorrosion of Cu2O. This work could provide new insight into the design and preparation of novel visible-light-responding semiconductor composites.