Ti-6Al-4V alloy powder was taken as raw material. 60%（mass fraction） paraffin, 35%low density polyethylene and 5%stearic acid were employed as binders to prepare injection feedstocks. Capillary rheometer was adopted to determine the rheological parameters and to analyze the rheological properties of the feedstocks at different milling time, powder loading and temperature. It is indicated through the results that the viscosity increases and the value of n decreases with the increase of milling time. The more the powder loading is, the higher the viscosity is. The empirical formula on the relationship between the viscosity and the powder loading is： ηr=η/ηb=A（1-Ф/Фmax）/^- m . The value m is calculated as 0.33. The flow activation energy Ea decreases with the increase of shear rate.
对七道次异步叠轧铜板采用220℃×30 m in和220℃×40 m in两种退火工艺,运用背散射电子衍射技术(EBSD)对两种铜板的再结晶程度、极图和织构进行了研究.结果表明:采用220℃×40 m in退火工艺的铜板再结晶较完全,其织构为明显的{100}〈001〉立方织构;而采用220℃×30 m in退火工艺的铜板内仍存在晶体缺陷,其织构为{123}〈412〉轧制织构,及少量的{100}〈001〉立方织构.