A series of Ti–Al–V titanium alloy bars with nominal composition Ti–7Al–5V ELI,Ti–5Al–3V ELI,commercial Ti–6Al–4V ELI and commercial Ti–6Al–4V were prepared.These alloys were then heat treated to obtain bimodal or equiaxed microstructures with various contents of primary a phase.Dynamic compression properties of the alloys above were studied by split Hopkinson pressure bar system at strain rates from 2,000 to 4,000 s-1.The results show that Ti–6Al–4V alloy with equiaxed primary a(ap)volume fraction of 45 vol%or 67 vol%exhibits good dynamic properties with high dynamic strength and absorbed energy,as well as an acceptable dynamic plasticity.However,all the Ti53ELI specimens and Ti64ELI specimens with ap of 65 vol%were not fractured at a strain rate of4,000 s-1.It appears that the undamaged specimens still have load-bearing capability.Dynamic strength of Ti–Al–V alloy can be improved as the contents of elements Al,V,Fe,and O increase,while dynamic strain is not sensitive to the composition in the appropriate range.The effects of primary alpha volume fraction on the dynamic properties are dependent on the compositions of Ti–Al–V alloys.
Rui LiuSong-Xiao HuiWen-Jun YeCheng-Lin LiYan-Yan FuYang YuXiao-Yun Song
Terminal ballistic tests using 7.62 mm armor-piercing incendiary （API） projectiles were performed to evaluate the resistance to penetration of Ti-5Al-5Mo-5V-3Cr-IZr （Ti-55531） alloy. The dynamic properties were determined by a split Hopkinson pressure bar （SHPB） test system. Ti-55531 plates were subjected to two kinds of heat treatments, leading to the formation of high-strength and high-toughness plates. The results of SHPB test exhibit that the maximum impact absorbed energy of the high-strength plate at a strain rate of 2200 s^-1 is 270 MJ/m^3; however, the maximum value for the high-toughness plate at a strain rate of 4900 s^-1 is 710 MJ/m^3. The ballistic limit velocities for the high-strength and high-toughness plates with dimensions of 300 mm×300 mm×8 mm are 330 and 390 m/s, respectively. Excellent dynamic properties of Ti-55531 alloy correspond to good resistance to penetration. The microstructure evolution related to various impact velocities are observed to investigate the failure mechanism.
Split Hopkinson pressure bar test system was used to investigate the plastic deformation behavior and dynamic response character of a-type Ti–5Al–2.5Sn ELI and near a-type Ti–8Al–1Mo–1V titanium alloy when subjected to dynamic loading. In the present work, stress–strain curves at strain rate from 1.5 9 103to 5.0 9 103s-1were analyzed, and optical microscope（OM） was used to reveal adiabatic shearing behavior of recovered samples. Results show that both the two alloys manifest significant strain hardening effects. Critical damage strain rate of the two alloys is about 4.3 9 103s-1, under which the impact absorbs energy of Ti–5Al–2.5Sn ELI and Ti–8Al–1Mo–1V are 560 and 470 MJ m-3, respectively. Both of them fracture along the maximum shearing strength orientation, an angle of 45° to the compression axis. No adiabatic shear band（ASB） is found in Ti–5Al–2.5Sn ELI alloy, whereas several ASBs with different widths exist without regular direction in Ti–8Al–1Mo–1V alloy.