It is a common method to strengthen the damaged RC structures with bonded steel plates. At present the ultimate bearing ca- pacity of RC structures strengthened with bonded steel plates is calculated mostly using the theory based on the test. Four beams, including one reference beam, two strengthened concrete beams in primary force and secondary force respectively, and one strengthened concrete beam which was not anchored enough, were tested under four-point bending (4PB) in order to get the data of strain of longitudinal bars, bonded bottom steel plate in tension and deflection of beams in the middle span. The experimental program was supported by a three-dimensioned finite analysis using ABAQUS. At the end of experiments and finite analysis, it is concluded that the investing strengthening technique can significantly improve the load-carrying capacity and the phenomenon of stress concentration at the end of interface, as well as the damage at interface, can be well simulated with cohesive element provided by ABAQUS.
The rigid body limit equilibrium method （LEM） and the nonlinear finite element method （NFEM） are often used in the analysis of anti-sliding stability of gravity dam. But LEM cannot reflect the process of progressive instability and mechanical mecha- nism on failure for rock mass while NFEM is difficult to use to solve the displacement discontinuity of weak structural plane. Combining the research with Xiangjiaba Hydropower Station project, the analysis of anti-sliding stability for segment 12# of the dam has been carried out using interface stress element method （ISEM）. The results can reflect the most dangerous location, the scope and distribution of failure zone in weak structural plane, and present the process of progressive failure in dam foun- dation as well as the safety coefficient of possible sliding body. These achievements provide an important technical reference for dam foundation treatment measures. The computational results show that ISEM can naturally describe discontinuous de- formation of rock mass such as dislocation, openness and sliding. Besides, this method is characterized by good adaptability, convenient calculation and high compatibility, thus it is regarded as an effective way to make an analysis of anti-sliding stabil- ity of gravity dam
An experimental investigation on the mechanical mechanisms of fatigue micro-crack initiation and propagation of a nickel-based superalloy is presented. By coupling digital image correlation method and scanning electron microscope, the fatigue residual strain distribution at the grain scale has been obtained. The results showed that there is a trend of accumulation for the residual strain. Micro-cracks are more likely to initiate in or near the areas with particularly large residual strain, and propagate along the large-strain paths.
Dong Lei 1 Kefeng Wang Qing Zhang Pizhong Qiao (State Key Laboratory of Hydrology-Water Resources and Hydraulic Engineering, Hohai University, Nanjing 210098, China) (College of Mechanics and Materials, Hohai University, Nanjing 210098, China)
Peridynamics (PD), a recently developed theory of solid mechanics, which employs a non-local model of force interaction and makes use of integral formulation rather than the spatial partial differential equations used in the classical continuum mechanics theory, has shown effectiveness and promise in solving discontinuous problems at both macro and micro scales. In this paper, the peridynamics theory is used to analyze damage and progressive failure of concrete structures. A non-local peridynamic model for a rectangular concrete plate is developed, and a central pairwise force function is introduced to describe the interior interactions between particles within some definite distance. Damage initiation, evolution and crack propagation in the concrete model subject to in-plane uni-axial tension, in-plane uni-axial compression and out-of-plane impact load are investigated respectively. The numerical results show that discontinuities appear and grow spontaneously as part of the solution to the peridynamic equations of motion, and no special failure criteria or re-meshing techniques are required, which proves the potential of peridynamic modeling as a promising technique for analyzing the progressive failure of concrete materials and structures.
HUANG Dan1,2, ZHANG Qing1,2 & QIAO PiZhong1,3 1 State Key Laboratory of Hydrology-Water Resources and Hydraulic Engineering, Hohai University, Nanjing 210098, China