Lithium-ion capacitors(LICs) were fabricated using mesocarbon microbeads(MCMB) as a negative electrode and a mixture of activated carbon(AC) and LiFePO4 as a positive electrode(abbreviated as LAC).The phase structure and morphology of LAC samples were characterized by X-ray diffraction(XRD) and field emission scanning electron microscopy(FESEM).The electrochemical performance of the LICs was studied using cyclic voltammetry,charge-discharge rate measurements,and cycle performance testing.A LIC with 30 wt% LiFePO4 was found to have the best electrochemical performance with a specific energy density of 69.02 W h kg-1 remaining at 4 C rate after 100 cycles.Compared with an AC-only positive electrode system,the ratio of practical capacity to theoretical calculated capacity of the LICs was enhanced from 42.22% to 56.59%.It was proved that adding LiFePO4 to AC electrodes not only increased the capacity of the positive electrode,but also improved the electrochemical performances of the whole LICs via Li+ pre-doping.
To investigate the influence of expansion pretreatment for materials on carbon structure, activated carbons （ACs） were prepared from corncob with/without expansion pretreatment by KOH activation, the structure properties of which were determined based on N2 adsorption isotherm at 77 K. The results show that the expansion pretreatment for corncobs is beneficial to the preparation of ACs with high surface area. The specific surface area of the AC derived from corncob with expansion pretreatment （AC-1） is 32.5% larger than that without expansion pretreatment （AC-2）. Furthermore, to probe the potential application of corncob-based ACs in electric double-layer capacitor （EDLC）, the prepared ACs were used as electrode materials to assemble EDLC, and its electrochemical performance was investi- gated. The results indicate that the specific capacitance of AC-I is 276 F/g at 50 mA/g, which increases by 27% com- pared with that of AC-2 （217 F/g）. As electrode materials, AC-1 presents a better electrochemical performance than AC-2, including a higher voltage maintenance ratio and a lower leakage current.