The luminous polypropylene fiber based on long afterglow luminescent material Sr2MgSi2O7：Eu^2＋,Dy^3＋was prepared by melt-spinning process. Micro-morphology, phase composition, crystal structure, spectral features and afterglow properties of the lu-minescent fiber were tested and analyzed. The results indicated that the fiber had independent superposition phase features of both Sr2MgSi2O7：Eu2＋,Dy3＋and polypropylene. The range of its excitation wavelength was located between 250-450 nm;therefore, the luminescent fiber could be excited by ultraviolet or visible light. It could emit blue light of 460 nm wavelength after excitation, which was caused by the 5d-4f transition of Eu^2＋ions within the host lattice. The initial luminescent intensity was more than 0.8 cd/m^2, and afterglow life lasted 7 h. The afterglow decay was composed of rapid-decaying and slow-decaying processes, and the decay charac-teristics depended on the depth and concentration of trap level in the Sr2MgSi2O7：Eu^2＋,Dy^3＋.