Formation and coexistence of tricalciurn silicate （C3S） and calcium sulphoaluminate （ C4 A3S^- ） minerals in Portland cement clinker containing calcium sulphoaluminate were investigated. Thef-CaO content, mineral composite and formation of mineral in the clinker were analyzed respectively by chemical analysis, differential scanning calorimetry（DSC） and X-ray diffraction. The results show that, adding a suitable amount of BaO can improve the burnability of raw meal and promote the f-CaO absorption. Tricalcium silicate and calcium sulphoaluminate minerals can form and coexist in clinkers at 1 234-1 317 ℃ by the addition of BaO to the raw meal. A suitable amount of BaO expanded the coexistence temperature of two minerals by 58 ℃.
Optimization of the content of tricalcium silicate（C 3 S）of high cementing clinker was investigated.The content of free-CaO（f-CaO）,mineral composite,the content of C 3 S in the clinker and the hydration product were analyzed by chemical analysis and X-ray diffraction（XRD）.＂K Value＂method of QXRD was selected as a quantitative analysis way to measure the content of C 3 S,and the strength of cement paste was determined.The results show that at a water cement ratio of 0.29,the strength of cement paste with 73%C 3 S can be up to 97.5 MPa at 28 days age.The strength at 28 d of cement with 73%C 3 S is 16%higher than that with 78%C 3 S at water requirement for normal consistency.The relationship between the strength of high cementing Portland cement and the content of C 3 S in the clinker is nonlinear.According to the strength of cement paste,the optimal content of C 3 S in cement clinker is around 73%in this paper.
A novel methodology for the formulation design of the multi-component cement additive for the low early strength blend cement was presented by using engineering statistics.Components of cement additive such as triethanolamine,chloride,saccharide and a kind of divalent alcohol were simultaneously tested according to the arrangement of response surface methodology.Mathematical models were established to express the quantitative relationship between the chemical components of cement additive and the compressive strength of treated blend cement.The effectiveness and the possible interactions of these four chemicals contributing to the strength development of blend cement were further explored by the pareto chart and the contour plot.Finally according the performance analysis of four chemicals,the optimized formulations were brought forward and were validated in practical trials by Turkey＇s multiple comparison.