In this paper we report the leakage current, ferroelectric and piezoelectric properties of the YFe O3 film with hexagonal structure, which was fabricated on Si（111） substrate by a simple sol-gel method. The leakage current test shows good characteristics as the leakage current density is 5.4 × 10^-6A/cm^2 under 5 V. The dominant leakage mechanism is found to be an Ohmic behavior at low electric field and space-charge-limited conduction at high electric field region. The P–E measurements show ferroelectric hysteresis loops with small remnant polarization and coercive field at room temperature.The distinct and switchable domain structures on the nanometer scale are observed by piezoresponse force microscopy,which testifies to the ferroelectricity of the YFe O3 film further.
The dielectric loss tanfi of half-doped manganite Lao.sCao.sMnO3 is investigated using Green＇s function technique. The Lao.sCao.sMnO3 is described by the Kondo-lattice model in the double exchange limit, taking into account the Jahn- Teller distortion and the super-exchange interaction between the localized electrons. It is found that the intensity of tans decreases with increasing [e]TI, V, and U. It is also observed that the transition temperature Tp rises as l eJTI and U increase. It is worth noting that Tp remains unchanged and the strength of tans increases with increasing g. The calculated dielectric loss results are explained theoretically, and these behaviors are in qualitative agreement with the experimental results.
An oxygen-deficient SrTiO3/La0.67Sr0.33MnO3 heterojunction is fabricated on an SrTiO3 （001） substrate by a pulsed laser deposition method. The electrical characteristics of the heterojunction are studied systematically in a temperature range from 80 K to 300 K. The transport mechanism follows I ∝ exp （eV/nkT） under small forward bias, while it becomes space charge limited and follows I ∝ Vm（T） with 1.49〈 m 〈1.99 under high bias. Such a heterojunction also exhibits magnetoresistance （MR） effect. The absolute value of negative MR monotonically increases with temperature decreasing and reaches 26.7% at 80 K under H=0.7 T. Various factors, such as strain and oxygen deficiency play dominant roles in the characteristics.