Four kinds of Ca-based sorbents were prepared by calcination and hydration reactions using different precursors： calcium hydroxide, calcium carbonate, calcium acetate monohydrate and calcium oxide. The CO2 absorption capacity of those sorbents was investigated in a fixed-bed reactor in the temperature range of 350-650 ℃. It was found that all of those sorbents showed higher capacity for CO2 absorption when the operating temperature higher than 450 ℃. The CaAc2-CaO sorbent showed the highest CO2 absorption capacity of 299 mg.g-1. The mor- phology of those sorbents was examined by scanning electron microscope （SEM）, and the changes of composition before and after carbonation were also determined by X-ray diffraction （XRD）. Results indicated that those sorbents have the similar chemical compositions and crystalline phases before carbonation reaction [mainly Ca（OH）2], and CaCO3 is the main component after carbonation reaction. The SEM morphology shows clearly that the sorbent pores were filled with reaction products after carbonation reaction, and became much denser than before. The N2 adsorption-desorption isotherms indicated that the CaAc2-CaO and CaCO3-CaO sorbents have higher specific surface area. lar2er oore volume and anoropriate pore size distribution than that of CaO-CaO and Ca（OH）2-CaO.
YANG Lei YU Hongbing WANG Shengqiang WANG Haowen ZHOU Qibin
This paper presents a new selective adsorbent to remove nitrogen-containing heterocyclic compounds from model and commercial transportation diesel fuels based on characteristic reaction designed to occur in the pores of substrate.This reactive adsorbent is composed of formaldehyde,phosphotungstic acid and Santa Barbara USA(SBA)-15.The experiment was based on assumed hydroxymethylation reaction of nitrogen-containing heterocyclic compounds with formaldehyde using phosphotungstic acid as catalyst in batch and fixed-bed systems.The nitrogen concentration in the model fuel was 237.33 ng.μl-1,carbazole and toluene were used as model nitrogen-containing heterocyclic compound and solvent,respectively.The effectiveness of reactive adsorbent for removal of nitrogen-containing heterocyclic compounds from commercial 0# diesel fuel containing 224.86 ng.μl-1 nitrogen was examined in a fixed-bed reactor at 70 ℃.The results showed that nitrogen in the model fuel was very low and the nitrogen concentration in the commercial diesel reduced to 2.44 ng.μl-1.The demand for transportation fuel with ultra-low nitrogen is satisfied.
In this work,hybrid material CNTs@MIL-101(Cr) was synthesized in 2 h using multi-walled carbon nanotubes(MWCNTs) as the crystal growth accelerator with hydrothermal method.The characteristic differences between the crystals of CNTs@MIL-101(Cr) and MIL-101 were investigated by N_2 adsorption–desorption isotherms,X-ray diffraction(XRD),scanning electron microscope(SEM) and thermogravimetric analyzer(TGA).The results showed that MWCNTs embedding in the hybrid material provide more mesoporous volumes than that of MIL-101.Moreover,the fast synthesized crystals of CNTs@MIL-101(Cr) still preserve the octahedral shape like MIL-101 and have a larger size ranging from 1.5 to 2.0 μm which were approximately three times larger than that of MIL-101.In the proposed mechanism,the roles of MWCNTs played in the crystallization were discussed where MWCNTs can be seen as coaxial cylindrical tubes composed of multi-layer graphenes and the place where nucleation and crystal growth processes occur at the tubes' out surface.Then,a crystal seeding layer bonding with the MWCNTs may be easily formed which accelerates the growth rate of MIL-101 crystals.Thus,larger crystals of CNTs@MIL-101(Cr) were formed due to the faster crystal growth rate of MIL-101.